UHMW – PE Sheets - Shibaam Polymers

UHMW – PE Sheets

UHMW-PE (ultra-high molecular weight polyethylene) sheets are a type of plastic that is known for its extremely high wear and abrasion resistance. It is also self-lubricating, has a low coefficient of friction, and is resistant to chemicals and moisture. Our commitment to engineering excellence is evident in every UHMW – PE Sheet we produce. Whether you seek wear resistance, low friction, or chemical resilience, our UHMW – PE Sheets are engineered to exceed your expectations and elevate your industry’s performance.

Product Description

Ultra-High Molecular Weight Polyethylene (UHMW-PE) is a high-performance thermoplastic known for its exceptional durability and unique combination of properties. With an extremely high molecular weight, UHMW-PE exhibits outstanding wear resistance, low friction, chemical inertness, and impact strength. This versatile material is self-lubricating, making it suitable for applications where reduced friction and wear are critical. UHMW-PE is commonly used in industries such as manufacturing, automotive, healthcare, and food processing due to its ability to withstand harsh conditions and provide reliable performance.

Features

Toughness and Durability
Ease of Fabrication
Impact Resistance
Chemical Resistance
Temperature Stability
Versatile Applications

Specifications

Standard Sizes

Sheet: Thickness X Width x Length
6-150mm x 1000mm X 2000mm
Rod: diameter x length
16-400mm X 1000mm

Customised sizes can be made to order

Properties

Exploring the Versatility of UHMW – PE Sheets Across Industries

Typical Application

Exploring the Versatility of UHMW – PE Sheets Across Industries

Products

Exploring the Versatility of UHMW – PE Sheets Across Industries

Mechanical Properties

Performance and Test Conditiom	Test Method	Unit	Tyical Values
Notched impact strength of cantilever beam, 23°C	ASTM D256	KJ/m²	8
Yield tensile strength, 23°C, 50mm/min	ASTM D638	Mpa	75
Elongation at break, 23°C, 50mm/min	ASTM D638	%	5
The bending strength. 23C, 2mm/min	ASTM 790	Mpa	90
Bending modulus, 23°C, 2mm/min	ASTM 790	Mpa	2200
Shore hardness D	ASTMD2240	–	80
The Density	ISO 1183	g/cm3	1.13

Thermal Properties

Performance and Test Conditiom	Test Method	Unit	Tyical Values
Thermal deformation temprature(HDT) (0.45Mpa)	ISO 75	°C	70
Melting point	–	°C	220
Long term operating temperature	–	°C	80
Short-term operating temperature	–	°C	110
Thermal conductivity	DIN 52612-1	W/(K-M)	0.23
Linear expansion coefficient	ASTM D696	10-5-1/K	8

Electrical Performance

Performance and Test Conditiom	Test Method	Unit	Tyical Values
Dielectric strength	ASTM D150	KV-mm	25
Dielectric loss coefficient	ASTM D150	–	0.032
The volume resistance	ASTM D257	Ω.cm	1015
The surface resistance	ASTM D257	Ω	1015
Dielectric constant	ASTM D149	–	4.2