Test Certificates

CAST NYLON RODS & SHEETS TEST CERTIFICATE

PRODUCT	Cast Nylon
Melting Temperature	2150C
Density	1.14-1.16g/cm3
Tensile strength at yield	750-850 kg/cm3
Elongation at yield	12-13%
E-modulus	24,000 to 26,300 kg/cm3
Hardness Rockwell 230C	R 107 -112
Durometre 230C	D 82-89
Temperature of deflection	800C
Compression Strength at yield	940 kg/cm3
Notched impact strength	5-11 kg cm/cm
Impact strength at +200C	10 kg cm/cm
Water absorption at 200C	0.3-3%
Flexural strength	1000-1350 kg/cm2
Resistance to heat (continuous)	In Air 800C In
	Water 1000C In Oil
	1400C
Effect of weak acids	Resistant
Effect of strong acids	Attacked
Effect of weak alkalies	None
Effect of strong alkalies	None
Effect of Organic Solvents	Resistant to common solvents

We confirmed that the above mentioned properties compliy with the material supplied

HDPE SHEET

SI. No	Parameter	Value
1	Density	0.948 g/cc
2	Apparent Bulk Density	0.59 g/cc
3	Water Absorption	0.01%
4	Hardness, Shore D	62
5	Tensile Strength, Ultimate	30 MPa
6	Tensile Strength, Yield	21.9 MPa
7	Elongation at Break	840%
8	Tensile Modulus	0.86 GPa
9	Flexural Modulus	0.928 GPa
10	Izod Impack, Notched	3.7 J/cm
11	Tensile Impack Strength	380 kJ/m2
12	Coefficient of Friction	0.28
13	Melting Point	130’C
14	Vicat Softening Point	120’C

POLYAMIDE- NYLON PA6 RODS

PRODUCT	PA6 NYLON RODS
DIA METER	6MM – 400MM
LENGTH	1 MTR
Melting Temperature	2150C
Density	1.14-1.16g/cm3
Tensile strength at yield	750-850 kg/cm3
Elongation at yield	12-13%
E-modulus	24,000 to 26,300 kg/cm3
Hardness Rockwell 230C	R 107 -112
Durometre 230C	D 82-89
Temperature of deflection	800C
Compression Strength at yield	940 kg/cm3
Notched impact strength	5-11 kg cm/cm
Impact strength at +200C	10 kg cm/cm
Water absorption at 200C	0.3-3%
Flexural strength	1000-1350 kg/cm2
Resistance to heat (continuous)	In Air 80 °C
	In Water 100°C
	In Oil 140°C
Effect of weak acids	Resistant
Effect of strong acids	Attacked
Effect of weak alkalies	None
Effect of strong alkalies	None
Effect of Organic Solvents	Resistant to common solvents

We confirmed that the above mentioned properties compliy with the material supplied

P U - POLYURETHANE TEST

Hardness (Shore A)	55A	60A	70A	75A	80A	85A	90 A	95A	95 D	60D	90+3
Tensile Strength /Mpa (psi)	19	10	7	10	19	21	31	32	34	35	30
100%Modules / Mpa(psi)	1.8		2.1	4.2	5.4	5.9	8.9	9.2	15.2	15.8	6.2(899)
300%Modules / Mpa(psi)	5.1		3.0	6.3	10.0	10.3	14.6	16.8	24.6	23	11.7(1697)
Angel Tear Strength (DIE C)(kN/m)( without nick)	26.0	38	34	44	53	57	73	78	95	120	70
Elongation(%)	680	700	600	550	500	480	460	450	440	420	440
DIN ABRASION RESISTANCE(mm3)	38		163	159	116	157	135	117	143	135	140
Specific Gravity	1.21	1.1	1.08	1.09	1.11	1.13	1.14	1.15	1.16	1.17	1.15
Rebount(%)	65	60	50	48	41	31	30	31	41	43	20

We confirmed that the above mentioned properties compliy with the material supplied

POM SHEET

ITEM	METHOD	UNIT	VALUE
Mechanical Properties
Specific gravity	ASTM D792	g/cm3	1.43
Tensile yield strength	ASTM D638	Mpa	60
Breaking elongation	ASTM D638	%	30
Bending strength	ASTM 790	Mpa	100
Flexural modulus	ASTM 790	Mpa	2800
Shore hardness	ASTM D2240	D	85
Impact strength	ASTM D256	J/M	74
Thermal Properties
Melting point	DSC	℃	165
Heat distortion temperature	ASTM D648	℃	130
Operating temperature	–	℃	100
Maximum operating temperature	–	℃	150
Thermal conductivity	DIN 52612-1	W/(K-M)	0.31
Coefficient of linear thermal expansion	ASTM D696	10-5-1/K	13
Electrical Properties
Dielectric strength	ASTM D150	KV-mm	19
Dielectric loss factor	ASTM D 150		0.01
Volume resistivity	ASTM D257	Ω.cm	1014
Surface resistivity	ASTM D 257	Ω	1016
Dielectric constant	ASTM D 149		3.7
Chemical Properties
Water absorption	23℃60%RH %	%
Acid resistance	23℃60%RH	+
Alkali resistance		+
Acid and alkali resistance		+
Resistance to sodium chlorate		0
Resistance to aromatic compounds		+
Resistance to ketone	23℃60%RH	+
Resistance to hot water	23℃60%RH	+
Others
Flammability	UL 94		HB
Viscosity
Non toxic +	EEC 90/128 FDA
Coefficient of friction	DIN53375		0.35
Anti-ultraviolet	₋		0

Remarks:
1.“+”: positive “-”: negative “0”: depends.
2. All the parameters above are based on raw material but not finished products,

PPHP DATA SHEET

Typical Characteristics
Property	Test Method	Unit	Typical Value
Melt Flow Rate (230°C/2.16kg)	ASTM D 1238	g/10 min	1.8
Tensile Strength at yield (50mm/min)	ASTM D 638	Mpa	27
Elongation at Yield (50mm/min)	ASTM D 638	%	11
Flexural Modulus (I% secant)	ASTM D 790A	MPa	1000
Notched Izod Impact Strength (23°C)	ASTM D 256	J/m	200
Heat Deflection Temperature (455 kPa)	ASTM D 648	°C	95

Remark:
The data mentioned in this Certificate are average values ascertained by current satistical returns and tests. The data above are provided purely for information and shall not be regarded as binding.

PP RODS

S. NO	PROPERTIES	SPECIFICATION	OBTAINED VALUE
1	VISUAL APPEARANCE	GOOD	GOOD
2	TENSILE STRENGTH @ YEILD	22-30 Mpa	24.1Mpa
3	ELONGATION YIELD	8-20 %	13%
4	ELONGATION BREAK	30%(Min)	480%
5	SPECIFIC GRAVITY	0.900 g/cc(Min)	0.918 g/cc
6	MELT FLOW RATE	0.2-4.1 gm/10 min	0.965 g/10 min
7	HARDNESS (SHORE – D)	67.75	69

PVC CURTAINS & SOFT SHEET

Report No:NSTQP[2010]CJ521 Precatory Code 201
Name Odf sample*			PVC strip curtain				Quantity of sample	1m
Type ans Specification						Date of Production	Date of Sampling	Jan 1-2015
Descriptions of Sample			Sample Is natural and transparence.
No	Iteam(s) tested				Units	Test Result(s)	Standars of test
1	Transmissinity				%	89	Coporation
2	Tensile strength MD/TD				Mpa	19.4/18.7	standard Q/HKSY
3	Ealongation at break MA/TD				%	617/727	01-2007″PVC”
4	rate of imensaional stability after heated
	80°C 12h
		TD			%	0.9
		MD			%	-3.4
5	foldebility at low temperature -20° 1h				…….	no Flaw
6	Water Absortivity method 1				g/cm²	0.13	GB/T 1034-1998
7	Tear Strength MD/TD				kN/m	65.3/65.1	QB/T 1030.1991
8	Vicat softening temprature			A50	°C	53	GB/T 1633-2000
9	Breakdown Voltage			short-time	KV	41.5	GB/T 1408.1-2006
10	Content of dissoluble Pb				Mg/m²	<1.0	GB/T 4615-1984

Approved By : Reviewed By : Compiled By : Date :

PVC RIGID SHEET

TEST ITEM	UNIT	RESULT	TEST METHOD
SPECIFIC GRAVITY	G/CM3	1.55-1.60	ASTM D792
TENSILE STRENGHT	KG/CM2	550	ASTM D638
IMPACT STRENGHT	KG.CM/CM	IZOD 4.0/CHARPY 7.0	ASTM D256
FLEXURAL STRENGHT	KG/CM2	960	ASTM D970
FLEXURAL MODULUS	KG/CM2	28000	ASTM D790
HARDNESS (ROCKWELL)	R	115	ASTM D785
DEFLECTION TEM ( HDT.264PSI)	C	76	ASTM D648
VICAT FLEXIBILITY TEMP (VSP 1 KG)	C	99	ASTM D1525
DIELECTRIC BREAKDOWN STRENGHT	KV/CM	350	ASTM D149
DIELECTRIC CONSTANT (F-IKHZ)	–	3.2	ASTM D150
DISSIPATION FACTOR (F-1KHZ)	–	0.02	ASTM D150
VOLUME RESISTIVITY	0.CM	3.5X10	ASTM D257

PVC Rods

Mechanical Properties
S. NO	PROPERTIES	TEST METHOD	UNIT	VALUE
1	Tensile Strength at Yield	ISO527	Mpa	57
2	Elongation at Yield	ISO527	%	3
3	Tensile strength at break	ISO527	Mpa	31
4	Elongation at break	ISO527	%	>=10
5	Impact strength	ISO179	KJ/M²	no break
6	Notch Impact strength	ISO179	KJ/M²	4
7	Ball Indentation / Roackwell hardness	ISO 2039-1	Mpa	120
8	Shore -D	DIN 53505		82
9	Flexural strength	ISO178	Mpa	90
10	Modulus of elastacity	ISO527	Mpa	3100

Thermal Properties
S. NO	PROPERTIES	TEST METHOD	UNIT	VALUE
1	Vicat- softening Point VST/B/50	ISO 306	°C	75
	VST/A/50		°C	–
2	Heat defiection temperature HDT/B	ISO 75	°C	72
	HDT/A		°C	–
3	Coefficient of linear thermal expansion	DIN 53752	k⁻¹+ 10⁻⁴	0.8
4	Thermal Conductivity at 20°C		W/(m+k)	4.014

PVC soft sheet

Performance test	Specification	Unit
Shore A Hardness	85+5	Sh A
Brittle Point	Approx -35	Degrees C
Thermal Conductivity	0.16	W/m.K
Vicat softening temp.	50	°C
Specific heat Capacity	1.6	kj/kg.K
Falling Ball Impact Test	“-20 No Break	Degrees C
Flexibility	“-20 No Break	Degrees C
Water Absorption	0.20%	%
Tensile Stress	340	%
Tearing resistance	50	N/mm
Reaction to Fire	Self – extinguishing	0
Sound reduction	>35	dB
Light Transmittance	86	%
Application	operating field , offices and restrooms , ware house , processing centers , manufacturing factory
Working temperature	“-20 to 50	°C

PP Sheet

Typical Characteristics
Property	Test Method	Unit	Typical Value
Melt Flow Rate (230°C/2.16kg)	ASTM D 1238	g/10 min	1.8
Tensile Strength at yield (50mm/min)	ASTM D 638	Mpa	27
Elongation at Yield (50mm/min)	ASTM D 638	%	11
Flexural Modulus (I% secant)	ASTM D 790A	MPa	1000
Notched Izod Impact Strength (23°C)	ASTM D 256	J/m	200
Heat Deflection Temperature (455 kPa)	ASTM D 648	°C	95

Remark:
The data mentioned in this Certificate are average values ascertained by current satistical returns and tests. The data above are provided purely for information and shall not be regarded as binding.

"KLIKPAD" NATURAL WHITE CUTTING BOARDS

Physical Properties	UNIT	DATA
Shore – Hardness D 3 sec	⁻⁻⁻	74-78
Notched impact strength 23° C/Charpi	mj⁄mm²	10
Modulus of elasticity in flexion	N⁄mm²	1350
Elongation at break	%	>100
Service temperature , short – time	°C	10⁄₊110
Coefficient of linear expansion	1⁄K	15.10⁻⁵
Specific Gravity	D 792	0.94 (+ 0.02)

THE PP LEVEL IN THE KLIKPAD CUTTING BOARD SUPPLIED IS 100% POLYPROPYLENE MATERIAL.

Remark:
The data mentioned in this Certificate are average values ascertained by current satistical returns and tests. The data above are provided purely for information and shall not be regarded as binding.

Handling:

Cutting depth on a newly planed surface max 0,3mm just to achieve the clean cut,no over cutting.
Increase the cutting depth gradually as needed, but as little as possible.
When reaching max.2mm cutting depth, please plane the board properly and leave the deepest cutting marks.
Planing cycles min.5 days ,12 days easly possible , the longer the better under the condition the surfaces is still in good shape and the cutting depth won’t exceed 2mm.
Flip and turn the boards alternately every 4 hours.
Use the entire surface evenly.
Horizontal storage on pallets or on the floor.
No radiation or exposure to sun light.

Test Certificates

CAST NYLON RODS & SHEETS TEST CERTIFICATE

We confirmed that the above mentioned properties compliy with the material supplied

HDPE SHEET

POLYAMIDE- NYLON PA6 RODS

We confirmed that the above mentioned properties compliy with the material supplied

P U - POLYURETHANE TEST

We confirmed that the above mentioned properties compliy with the material supplied

POM SHEET

Remarks:
1.“+”: positive “-”: negative “0”: depends.
2. All the parameters above are based on raw material but not finished products,

PPHP DATA SHEET

Remark:
The data mentioned in this Certificate are average values ascertained by current satistical returns and tests. The data above are provided purely for information and shall not be regarded as binding.

PP RODS

PVC CURTAINS & SOFT SHEET

PVC RIGID SHEET

PVC Rods

PVC soft sheet

PP Sheet

Remark:
The data mentioned in this Certificate are average values ascertained by current satistical returns and tests. The data above are provided purely for information and shall not be regarded as binding.

"KLIKPAD" NATURAL WHITE CUTTING BOARDS

THE PP LEVEL IN THE KLIKPAD CUTTING BOARD SUPPLIED IS 100% POLYPROPYLENE MATERIAL.

Trusted Partners: Brands We Are Associated With

Client Stories: A Tapestry of Satisfaction and Success

Global Exports: Connecting Countries, Delivering Quality.

Leading manufacturer in extrusion technologies of high performance engineering plastic products in India. The quality of our products and services is measured on the basis of national and International standards and guidelines

Useful Services

Contact Us

Follow Us on

Locate Us

UNIT - 1

UNIT - 2 & 3

Test Certificates

CAST NYLON RODS & SHEETS TEST CERTIFICATE

We confirmed that the above mentioned properties compliy with the material supplied

HDPE SHEET

POLYAMIDE- NYLON PA6 RODS

We confirmed that the above mentioned properties compliy with the material supplied

P U - POLYURETHANE TEST

We confirmed that the above mentioned properties compliy with the material supplied

POM SHEET

Remarks: 1.“+”: positive “-”: negative “0”: depends. 2. All the parameters above are based on raw material but not finished products,

PPHP DATA SHEET

Remark: The data mentioned in this Certificate are average values ascertained by current satistical returns and tests. The data above are provided purely for information and shall not be regarded as binding.

PP RODS

PVC CURTAINS & SOFT SHEET

PVC RIGID SHEET

PVC Rods

PVC soft sheet

PP Sheet

Remark: The data mentioned in this Certificate are average values ascertained by current satistical returns and tests. The data above are provided purely for information and shall not be regarded as binding.

"KLIKPAD" NATURAL WHITE CUTTING BOARDS

THE PP LEVEL IN THE KLIKPAD CUTTING BOARD SUPPLIED IS 100% POLYPROPYLENE MATERIAL.

Trusted Partners: Brands We Are Associated With

Client Stories: A Tapestry of Satisfaction and Success

Global Exports: Connecting Countries, Delivering Quality.

Leading manufacturer in extrusion technologies of high performance engineering plastic products in India. The quality of our products and services is measured on the basis of national and International standards and guidelines

Useful Services

Contact Us

Follow Us on

Locate Us

UNIT - 1

UNIT - 2 & 3

Remarks:
1.“+”: positive “-”: negative “0”: depends.
2. All the parameters above are based on raw material but not finished products,

Remark:
The data mentioned in this Certificate are average values ascertained by current satistical returns and tests. The data above are provided purely for information and shall not be regarded as binding.

Remark:
The data mentioned in this Certificate are average values ascertained by current satistical returns and tests. The data above are provided purely for information and shall not be regarded as binding.