Polyvinyl chloride (PVC) is a remarkable synthetic polymer that has revolutionized various industries with its exceptional properties and wide-ranging applications. This adaptable material offers a unique combination of durability, flexibility, and cost-effectiveness, making it a staple in construction, manufacturing, and everyday products.
Standard Sizes
Sheet: Thickness – 1mm-20mm
Sizes – 1mt x 2mt, 1.22mt x 2.44mt, 1.3mt x 2mt
Rod: Dia x Length- 6-300mm X 1000mm
Curtains: 200mm & 300mm width
Thickness – 2mm & 3mm
Soft sheet: 0.5 – 6mm x 1300mm x 10mt
Sizes can be customised to order
Utilized in the chemical and process industries to safely store, transport, and process various chemicals and liquids.
In industrial settings to channel and transport chemicals, acids, or liquids, ensuring safe and controlled conveyance.
Used in automation and electrical systems to house and components, monitoring, and management of machinery.
Used in industries like chemical processing and offshore oil platforms.
Utilized in the food industry to preserve and store perishable goods at controlled temperatures, preventing spoilage.
Used in healthcare to diagnose, and prevent diseases, improving patient health and well-being through the development.
Hospitality services to travelers and guests, offering a temporary home away from home for lodging, relaxation, and tourism.
Offer medical care, diagnostics, and treatment services to patients, addressing a wide range of illnesses and injuries.
| Performance and Test Conditiom | Test Method | Unit | Tyical Values |
| Notched impact strength of cantilever beam, 23°C | ASTM D256 | J/m | 450 |
| Yield tensile strength, 23°C, 50mm/min | ASTM D638 | Mpa | 50 |
| Elongation at break, 23°C, 50mm/min | ASTM D638 | % | 10 |
| The bending strength. 23C, 2mm/min | ASTM 790 | Mpa | 70 |
| Bending modulus, 23°C, 2mm/min | ASTM 790 | Mpa | 2400 |
| Shore hardness D | ASTMD2240 | – | 95 |
| The Density | ISO 1183 | g/cm3 | 1.4 |
| Performance and Test Conditiom | Test Method | Unit | Tyical Values |
| Thermal deformation temprature(HDT) (0.45Mpa) | ISO 75 | °C | 70 |
| Melting point | – | °C | 120 |
| Long term operating temperature | – | °C | 60 |
| Short-term operating temperature | – | °C | 90 |
| Thermal conductivity | DIN 52612-1 | W/(K-M) | – |
| Linear expansion coefficient | ASTM D696 | 10-5-1/K | 8 |
| Performance and Test Conditiom | Test Method | Unit | Tyical Values |
| Dielectric strength | ASTM D150 | KV-mm | 30 |
| Dielectric loss coefficient | ASTM D150 | – | – |
| The volume resistance | ASTM D257 | Ω.cm | 1014 |
| The surface resistance | ASTM D257 | Ω | 1016 |
| Dielectric constant | ASTM D149 | – | 2.4 |